AM90 Geschmolzenes Aluminiumoxid-Magnesia-Spinell

Der hochreine geschmolzene Aluminiumoxid-Magnesia-Spinell der Marke „Jun“ verwendet hochreine Magnesia und wird industriell in großen Hochtemperatur-Lichtbogenöfen geschmolzen. Er weist eine hohe Dichte, hohe Feuerfestigkeit und eine gute Hochtemperatur-Volumenstabilität auf.

The "Jun brand high-pure fused alumina magnesia spinel use high -pure magnesia and industrial alumina smelting by large high -temperature electric arc furnaces. lt has high density, high refractory resistance, and good hightemperature volume stability, anti alkaline slag erosion and permeability, good thermal stability and other characteristics. lt is widely used for steelmaking electric
furnace top, converter, ladle and porous plug brick/ladle well block, RH spinel brick/back lining castable, tundish current stabilizer & impacting plate board,transition zone of large cement rotary kiln & burnning zone, smelting alloy and glass heat storage rooms, lithium battery saggar and special plasma spray coatings.
Die Zugabe von Aluminiumoxid-Magnesia-Spinellen zu feuerfesten Gussmassen kann die Fließfähigkeit, Durchdringungs-, Erosions- und Abschälfestigkeit der Gussmassen deutlich verbessern. Insbesondere kann dies die Abwaschbeständigkeit verbessern, die Lebensdauer verlängern und den Bedarf an feuerfestem Material pro Tonne Stahl reduzieren. Außerdem wird das Problem der Rissbildung in Materialien gelöst, das durch die Zugabe von Magnesia-Rohstoffen verursacht wird.

Physikalische Eigenschaften und chemische Zusammensetzung

Artikel/Zusammensetzung	AL₂O₃	MgO	CaO	SiO₂	Fe₂O₃	Na₂O	Schüttdichte (g/cm)
AM-65	64 ~ 66	33 ~ 35	≤ 0.65	≤ 0.50	≤ 0.40	≤ 0.30	≥3.3
AM-70	74 ~ 76	23 ~ 25	≤ 0.55	≤ 0.40	≤ 0.40	≤ 0.30	≥3.2
AM-90	87 ~ 90	9 ~ 12	≤ 0.30	≤ 0.25	≤ 0.30	≤ 0.40	≥3.3
Partikelgröße	0~0.2~0.5~1~2~3~5~8mm,100 mesh、200 mesh、325 mesh、5μm
Prüfnorm	GB5069-2001
Packing	Innerer Kunststoff und äußeres Gewebe 25 kg/Beutel (kann nach Kundenwunsch angepasst werden)